0.40mm Green AFP Galvalume Steel GL Stone Coated Tiles Villa Roof
55% Aluzinc Steel Roof Panels DX51D ASTM A792M S280GD
55% Aluzinc steel coils, also known as Galvalume or Aluminium-Zinc alloy coated steel, are a type of steel coated with an alloy comprising approximately 55% aluminum, 43.4% zinc, and 1.6% silicon. This unique coating provides a combination of the excellent corrosion resistance of aluminum and the galvanic protection of zinc, making it a superior material for various applications.
Composition:
- Aluminum (55%): Provides exceptional corrosion resistance by forming a protective layer of aluminum oxide.
- Zinc (43.4%): Offers sacrificial protection, similar to traditional galvanized steel, protecting the steel substrate by corroding preferentially.
- Silicon (1.6%): Enhances adhesion of the coating to the steel and helps maintain the integrity of the alloy layer during fabrication.
- Advantages of Galvalume Steel Compared to Galvanized Steel
When comparing lightweight steel keels, one must consider the differences in scratch resistance and durability between galvanized and aluminium-zinc plated steel.
Differences Between Galvanized and Aluminium-Zinc Plating:
Galvanized Steel:
- Coating and Usage: Galvanized light steel coatings vary based on their intended environment and required corrosion resistance. The zinc coating can range from 120g/m² to 275g/m².
- Designation: For example, Z275 refers to galvanized steel with a total zinc coating weight of 275g/m² on both sides.
- Physical Changes: Over time, galvanized steel exposed to the elements will react with oxygen, causing the surface to blacken.
Aluminium-Zinc Plated Steel (Galvalume):
- Corrosion Resistance: Aluminium-zinc plated steel offers superior corrosion resistance, three times that of pure galvanized steel. This is due to the formation of a dense aluminium oxide layer that prevents further corrosion.
- Aesthetics: It features attractive zinc flowers on the surface, making it suitable for use as building exterior panels.
- Designation: AZ150 is a common abbreviation for aluminium-zinc plated steel, indicating a specific coating weight.
- Durability: The aluminium component provides excellent protection against chemical corrosion and physical reactions, maintaining the keel's appearance and preventing rust over time.
- Field Testing: Aluminium-zinc plated steel has undergone over 20 years of outdoor exposure tests in various atmospheric conditions, proving its superior edge protection compared to galvanized steel.
Heat Reflectivity:
- Aluminium-zinc plated steel has twice the thermal reflectivity of galvanized steel, making it an excellent thermal insulator. This property enhances its suitability for applications where heat reflection is beneficial.
In summary, aluminium-zinc plated steel, or Galvalume, offers enhanced corrosion resistance, better aesthetic longevity, and superior thermal reflectivity compared to traditional galvanized steel, making it a more durable and versatile choice for various applications.
1) Standard: ASTM A792M, AS1397, EN10346/ EN10143 all according to the customer's request
2) Grade: SGCC, CS-Type B, Grade 350, G550, Grade 50, Grade 80, SS550GD, all according to the customer's request
3) Capacity: about 20000 tons per month
4) Thickness: from 0.13mm to 2mm, all available
5) Width: from 600mm to 1250mm, regular size:750-762mm,900-914mm,1000mm,1200mm,1219-1250mm all available
6) Coil ID: 508mm
7) Coil weight: from 2-10MT, according to the customer's request
8) Zinc coating weight: AZ30~AZ165g/m2
9) Spangle: regular spangle,big spangle, small spangle
10) Surface treatment: Anti-finger print (Green, Blue, Golden, No color) Chemical passivating, oils, passivating oils,skin passed
11) Edge: mill edge, cut edge
12) Min trial order 25 ton each thickness
Detailed Parameters:
| SURFACE TREATMENT | DESCRIPTION OF USE |
| CHROMATE PASSIVATION(C) | Surface treatment for high-strength steel plates after hot-dip plating to reduce white rust during transport and storage |
| Chrome-free passivation(C5) | Surface treatments that require limiting the amount of hexavalent chromium, etc. in passivation solutions that are harmful to the environment and humans |
| Anti-finger print(N) | Surface treatment after the passivation process, which acts as a lubricant during processing, prevents fingerprints from staining during operation, and prevents premature blackening of the surface during use. |
| Chrome-free and fingerprint resistant(N5) | Surface treatment after the passivation process, in the process of lubrication, to prevent the operation of the fingerprint staining, to prevent the use of the surface of the process of premature blackening, and at the same time, the requirement to limit the fingerprint-resistant film harmful to the environment and human body, such as hexavalent chromium content |
| Oiled(O) | Surface treatment added after the passivation process to further reduce rusting during long-distance transport and long-term storage |
| Usage | Steel Grade | Yield Strength(MPa) | Tensile Strength(MPa) | Elongation at break A80mm % ≥ |
| Generally used | DC51D+AZ | 190～360 | 270～500 | 22 |
| stamping | DC52D+AZ | 140～300 | 270～420 | 26 |
| deep drawing | DC53D+AZ | 140～260 | 270～380 | 30 |
| extra-deep washout | DC54D+AZ | 120～220 | 260～350 | 36 |